L-901
Woven Graphite Adhesive Prepreg
Click For
Page 2
Product Data Sheet Revised 12/21/06
Description

L-901 is a 250°F (121°C) curing, high peel strength, flame retardant, epoxy prepreg available on a broad range of graphite fabrics or hybrid fabrics. L-901 is intended to be used as a single ply or multiple ply skin for aramid/phenolic honeycomb, fiberglass honeycomb or PVC foam core sandwich panels.

Advantages of L-901
  • No adhesive is required because of the high peel strength and high toughness of the L-901 resin matrix. L-901 can be bonded directly to a variety of core materials.
  • Easy processing is another major advantage. L-901 can be cured with vacuum bag, press or autoclave type cures from 90 minutes at 235°F (113°C) or in just 40 minutes at 275°F (135°C) with contact pressure (235°F (113°C) cure temperatures are recommended for urethane or PVC core).
  • L-901 is also an excellent laminating prepreg when high impact strength and toughness are required.
  Physical Properties on7 mile Graphite Fabric
  • Standard Weight: 0.067 lbs/ft2 (335 g/m2)
  • Standard Resin Content: 42% by weight
  • Standard Tack: Slightly tacky on one side
  • Cured Ply Thickness: 0.007” (0.178 mm)
  • Other Weights, Resin Contents, and Fabrics are Available.
Flammability
  • Self Extinguishing per FAR part 25.853
 Availability
  • Up to 60” width in rolls up to 100 yards long (152 cm x 91 m)
Shelf Life
  • 6 months at 40°F (4°C) or below
  • 7 days at Room Temperature (70°F or 21°C)
Cure Cycles
  • 40 minutes at 275°F (135°C), or
  • 60 minutes at 250°F (121°C), or
  • 90 minutes at 235°F (113°C).
Click For Page 2

NOTICE:Product data and parameters cited in this publication have been obtained in J.D. Lincoln, Inc. laboratories using the materials under carefully controlled conditions. The information, therefore, is believed to be accurate and correctly stated. Data of this type may be considered to be indicative of representative properties obtainable. J.D. Lincoln, Inc. cannot accept responsibility for the misapplication of these products, nor for their use under uncontrolled conditions. Numerical values resulting from the application of this material are dependant on processing details. It is recommended that the user develop his or her own application techniques and generate data consistent with his or her specific application and process.

 
       
Website Copyright 1996-2008 by J.D. Lincoln Inc.