| Mechanical Data |
|
LAMINATE PROPERTIES |
PROPERTY |
L-802, Grade B |
3K70P Carbon
1 Ply Facings
|
7781 Glass 1 Ply Facings |
7781 Glass 2 Ply Facings |
Facing Weight (lbs/ft2 ) |
0.095 |
0.102 |
0.103 |
0.196 |
Facing Weight (g/m2 ) |
464 |
498 |
503 |
957 |
Facing Thickness (inches) |
0.010 |
0.010 |
0.010 |
0.020 |
Facing Thickness (mm) |
0.254 |
0.254 |
0.254 |
0.254 |
Aramid Phenolic Honeycomb (in.-lb/ft3) |
0.125-3 |
0.125-3 |
0.125-3 |
0.125-3 |
Aramid Phenolic Honeycomb (mm-kg/m3 ) |
3.18-48 |
3.18-48 |
3.18-48 |
3.18-48 |
Panel Weight (lbs/ft2 ) |
0.285 |
0.299 |
0.301 |
0.487 |
Panel Weight (g/m2 ) |
1392 |
1460 |
1470 |
2378 |
Panel Thickness (inches) |
0.400 |
0.400 |
0.400 |
0.400 |
Panel Thickness (mm) |
10.2 |
10.2 |
10.2 |
10.2 |
Long Beam Flexure (lbf) |
150 |
118 |
88 |
175 |
Long Beam Flexure (N) |
667 |
525 |
391 |
778 |
Climbing Drum Peel (in-lbs/3 in) |
15 |
15 |
15 |
15 |
Climbing Drum Peel (N/76.2 mm) |
67 |
67 |
67 |
67 |
1” Dia Impact (in-lbs) |
125 |
25 |
35 |
75 |
1” Dia Impact (N) |
556 |
111 |
156 |
334 |
Facing Stress Ultimate (KSI) |
38 |
30 |
22 |
22 |
Facing Stress Ultimate (MPa) |
0.26 |
0.21 |
0.15 |
0.15 |
Facing Modulus (MSI) |
10 |
8 |
3 |
3 |
Facing Modulus (GPa) |
69 |
55 |
21 |
21 |
Insert Pullout (lbf) |
250 |
190 |
190 |
275 |
Insert Pullout (N) |
1112 |
845 |
845 |
1223 |
Insert Bearing (lbf) |
275 |
200 |
200 |
300 |
Insert Bearing (N) |
1223 |
890 |
890 |
1334 |
OSU Burn Average (kW/m2 ) |
54 |
59 |
50 |
45 |
OSU Burn Peak (kW/m2 ) |
48 |
63 |
50 |
45 |
|
| |
|
|
NOTICE:Product data and parameters cited in this publication have been obtained in J.D. Lincoln, Inc. laboratories using the materials under carefully controlled conditions. The information, therefore, is believed to be accurate and correctly stated. Data of this type may be considered to be indicative of representative properties obtainable. J.D. Lincoln, Inc. cannot accept responsibility for the misapplication of these products, nor for their use under uncontrolled conditions. Numerical values resulting from the application of this material are dependant on processing details. It is recommended that the user develop his or her own application techniques and generate data consistent with his or her specific application and process.
|
|
|