L-324
Two-component Past Adhesive, High Toughness
Click For
Page 1
 Shelf Life
  • 12 months at Room Temperature (75°F or 24°C)
Cure Cycles
  • Full Cure: 7 days at Room Temperature (75°F or 24°C)
  • Handling Strength: 24 hours at Room Temperature (75°F or 24°C)
  • Accelerated Cure: 2 hours at 150°F (65°C)
  Mixing Procedure
  • Combine 2 Parts A with 1 Part B (by weight) and mix thoroughly. If necessary, Part A may be pre-heated (up to 120F or 49C) to reduce the viscosity and allow for easier mixing. Apply immediately to bondline.
  Mechanical Properties
Tensile Shear Strength (ASTM D 1002)
  • -67F (-55C) 3300 PSI (22.7 MPa)
  • RT 3400 PSI (23.4 MPa)
  • 160F (71C) 1000 PSI (6.9 MPa)
T-Peel Using 0.020
  • (0.51 mm) Thickness Aluminum
    • RT 45 in lb/in (200 N/25 mm)
    Flatwise Tensile Strength with 1/8", 8 lbs/ft3 (3.175 mm, 128 kg/m3) Aluminum Core
    • RT 1320 PSI (9.1 MPa)
    • CAUTION: Care should be taken with batches over 500 grams total weight. Large batches or those which are mixed in excess of recommended ratios may become exothermic (i.e., VERY HOT). The user is encouraged to develop standard batch mix sizes.

    NOTICE:Product data and parameters cited in this publication have been obtained in J.D. Lincoln, Inc. laboratories using the materials under carefully controlled conditions. The information, therefore, is believed to be accurate and correctly stated. Data of this type may be considered to be indicative of representative properties obtainable. J.D. Lincoln, Inc. cannot accept responsibility for the misapplication of these products, nor for their use under uncontrolled conditions. Numerical values resulting from the application of this material are dependant on processing details. It is recommended that the user develop his or her own application techniques and generate data consistent with his or her specific application and process.

    		 
           