L-324LV
Two-component Paste Adhesive, High Toughness, Low Viscosity
Click For
Page 1
  Availability
  • 1 Gallon (3.8 L) Kit: 8 lbs Part A, 3.2 lbs Part B (3.6 kg Part A, 1.5 kg Part B)
  • 5 Gallon (18.9 L) Kit: 40 lbs Part A, 16 lbs Part B (18.1 kg Part A, 7.3 kg Part B)
 Shelf Life
  • 12 months at Room Temperature (75°F or 24°C)
Cure Cycles
  • Full Cure: 5 days at Room Temperature (75°F or 24°C)
  • Handling Strength: 16 hours at Room Temperature (75°F or 24°C)
  • Accelerated Cure: 2 hours at 150°F (65°C)
  Mixing Procedure
  • Combine 100 Parts A with 40 Part B (by weight) and mix thoroughly. Apply immediately to bondline.
  Mechanical Properties
Tensile Shear Strength (ASTM D 1002)
  • -67°F (-55°C) 4050 PSI (27.9 MPa)
  • RT 4230 PSI (29.2 MPa)
  • 180°F (82°C) 980 PSI (6.8 MPa)
T-Peel Using 0.020 (0.51 mm) Thickness Aluminum
  • RT 35 in lb/in (156 N/25 mm)
Compressive Strength ( ASTM D695)
  • RT 7300 PSI (50.3 MPa)
CAUTION: Care should be taken with batches over 500 grams total weight. Large batches or those which are mixed in excess of recommended ratios may become exothermic (i.e., VERY HOT). The user is encouraged to develop standard batch mix sizes.

NOTICE:Product data and parameters cited in this publication have been obtained in J.D. Lincoln, Inc. laboratories using the materials under carefully controlled conditions. The information, therefore, is believed to be accurate and correctly stated. Data of this type may be considered to be indicative of representative properties obtainable. J.D. Lincoln, Inc. cannot accept responsibility for the misapplication of these products, nor for their use under uncontrolled conditions. Numerical values resulting from the application of this material are dependant on processing details. It is recommended that the user develop his or her own application techniques and generate data consistent with his or her specific application and process.

 
       