Property |
25 PSI (0.17 MPa) Cure in Platen Press |
Press Cure after 1 Month Outlife |
Test Method |
|
|
|
|
|
Tensile Shear Strength |
|
|
|
-67°F (-55°C) |
6,700 PSI (46.2 MPa) |
6,680 PSI (46.0 MPa) |
ASTM D1002 |
Room Temp |
5,900 PSI (40.6 MPa) |
5,950 PSI (41.0 MPa) |
ASTM D1002 |
180°F (82°C) |
4,600 PSI (31.6 MPa) |
4,500 PSI (31.0 MPa) |
ASTM D1002 |
250°F (121°C) |
2,250 PSI (15.5 MPa) |
2,000 PSI (13.8 MPa) |
ASTM D1002 |
|
|
|
|
Sandwich Peel Strength |
|
|
|
-67°F (-55°C) |
42 in lb/in (187 N/25mm) |
40 in lb/in (178 N/25 mm) |
ASTM D1781 |
Room Temp |
39 in lb/in (173 N/25mm) |
35 in lb/in (156 N/25 mm) |
ASTM D1781 |
180°F (82°C) |
35 in lb/in (156 N/25 mm) |
32 in lb/in (142 N/25 mm) |
ASTM D1781 |
|
|
|
|
Flatwise Tensile Strength |
|
|
|
-67°F (-55°C) |
1,250 PSI (8.6 MPa) |
1,140 PSI (7.9 MPa) |
ASTM C297 |
Room Temp |
1,120 PSI (7.7 MPa) |
1,100 PSI (7.6 MPa) |
ASTM C297 |
180°F (82°C) |
660 PSI (4.5 MPa) |
620 PSI (4.3 MPa) |
ASTM C297 |
|
|
|
|
Sandwich Flexural Strength |
|
|
|
-67°F (-55°C) |
core failure |
core failure |
ASTM C393 |
Room Temp |
core failure |
core failure |
ASTM C393 |
180°F (82°C) |
core failure |
core failure |
ASTM C393 |
|
|
|
|
T-Peel Strength |
|
|
|
-67°F (-55°C) |
52 in lb/in (231 N/25 mm) |
50 in lb/in (223 N/25 mm) |
ASTM D1876 |
Room Temp |
49 in lb/in (218 N/25 mm) |
47 in lb/in (209 N/25 mm) |
ASTM D1876 |
180°F (82°C) |
41 in lb/in (182 N/25 mm) |
40 in lb/in (178 N/25 mm) |
ASTM D1876 |
|
|
|
|
Floating Roller Peel Strength |
|
|
|
-67°F (-55°C) |
105 in lb/in (467 N/25mm) |
104 in lb/in (463 N/25 mm) |
ASTM D3167 |
Room Temp |
95 in lb/in (423 N/25 mm) |
94 in lb/in (418 N/25 mm) |
ASTM D3167 |
180°F (82°C) |
85 in lb/in (378 N/25 mm) |
82 in lb/in (365 N/25 mm) |
ASTM D3167 |