L-313
Epoxy Film Adhesive, High Temperature Resistant |
|
|
| Mechanical Properties |
0.150 PSF ( 732 GSM) FILM |
PROPERTY |
295°F CURE |
350°F CURE |
TEST METHOD |
|
|
|
|
DOUBLE OVERLAP SHEAR |
|
|
|
STRENGTH |
|
|
|
|
|
|
|
-67°F (-55°C) |
6,750 PSI (46.5 MPa) |
6,850 PSI (47.2 MPa) |
FMS 3018 |
ROOM TEMP |
7,250 PSI (50.0 MPa) |
7,300 PSI (50.3 MPa) |
FMS 3018 |
270°F (132°C) |
5,100 PSI (35.2 MPa) |
5,250 PSI (36.2 MPa) |
FMS 3018 |
350°F (176°C) |
--- |
3,700 PSI (25.5 MPa) |
FMS 3018 |
|
|
|
|
FLATWISE TENSILE |
|
|
|
STRENGTH |
|
|
|
|
|
|
|
-67°F (-55°C) |
5,750 PSI (39.6 MPa) |
5,950 PSI (41.0 MPa) |
FMS 3018 |
ROOM TEMP |
5,400 PSI (37.2 MPa) |
5,550 PSI (38.3 MPa) |
FMS 3018 |
270°F (132°C) |
3,900 PSI (26.9 MPa) |
4,400 PSI (30.3 MPa) |
FMS 3018 |
350°F (176°C) |
--- |
2,900 PSI (20.0 MPa) |
FMS 3018 |
|
|
|
|
BEAM SHEAR |
|
|
|
STRENGTH |
|
|
|
|
|
|
|
ROOM TEMP |
850 PSI (5.9 MPa) |
860 PSI (5.9 MPa) |
FMS 3018 |
270°F (132°C) |
775 PSI (5.3 MPa) |
790 PSI (5.4 MPa) |
FMS 3018 |
350°F (176°C) |
--- |
700 PSI (4.8 MPa) |
FMS 3018 |
|
|
|
|
SINGLE OVERLAP SHEAR |
|
|
|
STRENGTH |
|
|
|
|
|
|
|
-67°F (-55°C) |
3,600 PSI (24.8 MPa) |
3,700 PSI (25.4 MPa) |
FMS 3018 |
ROOM TEMP |
3,600 PSI (24.8 MPa) |
3,650 PSI (25.1 MPa) |
FMS 3018 |
270°F (132°C) |
3,000 PSI (20.7 MPa) |
3,100 PSI (21.4 MPa) |
FMS 3018 |
350°F (176°C) |
--- |
2,490 PSI (17.2 MPa) |
FMS 3018 |
|
|
|
NOTICE:Product data and parameters cited in this publication have been obtained in J.D. Lincoln, Inc. laboratories using the materials under carefully controlled conditions. The information, therefore, is believed to be accurate and correctly stated. Data of this type may be considered to be indicative of representative properties obtainable. J.D. Lincoln, Inc. cannot accept responsibility for the misapplication of these products, nor for their use under uncontrolled conditions. Numerical values resulting from the application of this material are dependant on processing details. It is recommended that the user develop his or her own application techniques and generate data consistent with his or her specific application and process.
|
|
|